Pengaruh Variasi Temperatur Pengovenan Powder Coating Terhadap Laju Korosi Pada Baja Astm A36

Rizqi Sya'roni, Muhammad (2025) Pengaruh Variasi Temperatur Pengovenan Powder Coating Terhadap Laju Korosi Pada Baja Astm A36. Undergraduate thesis, Politeknik Negeri Jember.

[img] Text (Abstract)
abstrac.pdf - Submitted Version
Available under License Creative Commons Attribution Share Alike.

Download (187kB)
[img] Text (Bab 1 Pendahuluan)
pendahuluan 1.pdf - Submitted Version
Available under License Creative Commons Attribution Share Alike.

Download (168kB)
[img] Text (Daftar Pustaka)
daftar pustaka-1.pdf - Submitted Version
Available under License Creative Commons Attribution Share Alike.

Download (149kB)
[img] Text (Laporan Lengkap)
laporan lengkap.pdf
Restricted to Registered users only

Download (2MB) | Request a copy

Abstract

Powder coating is one of the effective metal coating methods to prevent corrosion, but the success of this coating is highly dependent on the drying or curing process. In this study, ASTM A36 steel was powder coated and dried at three variations of oven temperatures, namely 100°C, 150°C, and 200°C. After the drying process, the specimens were immersed in sulfuric acid solution (H₂SO₄) for 15 days to test corrosion resistance. The results of the study showed that the higher the oven temperature, the lower the corrosion rate. At a temperature of 100°C, the corrosion rate reached 0,0369 mm/y, while at 150°C it dropped to 0,0085 mm/y, and at a temperature of 200°C it became the lowest at 0,0028 mm/y. From the results of visual observations, it was also seen that the specimens dried at a temperature of 200°C experienced the least surface damage. Results of Conclusion, higher oven temperature can improve the quality of coating layer and corrosion resistance. This research is expected to be a reference for industry in determining the optimal drying temperature in powder coating process, especially for ASTM A36 steel.

Item Type: Thesis (Undergraduate)
Contributors:
ContributionContributorsNIDN/NIDK
Thesis advisorAzhar, Faruq AveroNIP199204172022031006
Uncontrolled Keywords: Powder Coating, Suhu Pengovenan, Korosi, Baja ASTM A36
Subjects: 410 - Rumpun Ilmu Teknik > 430 - Ilmu Keteknikan Industri > 431 - Teknik Mesin (dan Ilmu Permesinan Lain)
Divisions: Jurusan Teknik > Prodi D4 Mesin Otomotif > Tugas Akhir
Depositing User: Muhammad Rizqi Syaroni
Date Deposited: 06 Aug 2025 02:35
Last Modified: 06 Aug 2025 02:36
URI: https://sipora.polije.ac.id/id/eprint/45373

Actions (login required)

View Item View Item